Solubility: insoluble in water, Pigment Yellow 14 slightly soluble in toluene; in concentrated sulfuric acid was bright red orange, diluted into dark green light yellow precipitate.
Hue or shade: red and yellow
Relative density: 1.14-1.52
Bulk density / (lb / gal): 9.5-12.6
Melting point / ℃: 320-336
Average particle size / μm: 0.12
Specific surface area / (m2 / g): 35; 53 (BRM)
PH / (10% slurry): 5.0-7.5
Oil absorption / (g / 100g): 29-75
Red yellow powder, bright shade. A melting point of 336 ° C and a density of 1.35 to 1.64 g / cm 3. Strong color, good transparency, Pigment Yellow 14 the application performance are good, is one of the important varieties of benzidine. Melting point: - Relative density: 1.32g / cm3 Solubility: -
Pigment Yellow 14 Use and Synthesis Methods
Chemical nature: red yellow powder, shiny bright. A melting point of 336 ° C and a density of 1.35 to 1.64 g / cm 3. Strong color, good transparency, the application performance are good, is one of the important varieties of benzidine.
Uses: mainly used for rubber and plastic coloring, but also for polyurethane synthetic leather, high-grade ink and coatings.
Uses: mainly used for coloring plastic and rubber products, Pigment Yellow 14 but also for polyurethane synthetic leather, high-grade ink and paint coloring
Uses: mainly used for printing color paste color
Pigment Yellow 14 grades have 134 kinds. The importance of CI pigment yellow 12, pigment yellow 13 slightly worse than the pigment yellow 12 slightly green; compared to the European standard color standards to be green; color strength than CI pigment yellow 13 low, light fastness 1-2 ; Transparent Irgalite yellow BAW specific surface area of 55m2 / g; solvent resistance, good resistance to paraffin, especially in the United States for a large number of packaging ink. The amine-treated preparation is suitable for use in the publication of special formulations for gravure printing, with a pure color, but with strong green light. Pigment Yellow 14 The variety is less used for paint coloring; for polyolefins, heat up to 200 ℃, in a soft PVC over a certain concentration of frosting phenomenon; can also be used in elastomers, rubber coloring; can be used for viscose fiber and stick Rubber sponge